Jump to ContentJump to Main Navigation
Strengthening Mechanisms in Crystal Plasticity$
Users without a subscription are not able to see the full content.

Ali Argon

Print publication date: 2007

Print ISBN-13: 9780198516002

Published to Oxford Scholarship Online: September 2007

DOI: 10.1093/acprof:oso/9780198516002.001.0001

Show Summary Details
Page of

PRINTED FROM OXFORD SCHOLARSHIP ONLINE (www.oxfordscholarship.com). (c) Copyright Oxford University Press, 2019. All Rights Reserved. Under the terms of the licence agreement, an individual user may print out a PDF of a single chapter of a monograph in OSO for personal use (for details see www.oxfordscholarship.com/page/privacy-policy).date: 25 June 2019

OVERVIEW OF STRENGTHENING MECHANISMS

OVERVIEW OF STRENGTHENING MECHANISMS

Chapter:
(p.70) 3 OVERVIEW OF STRENGTHENING MECHANISMS
Source:
Strengthening Mechanisms in Crystal Plasticity
Author(s):

A. S. Argon

Publisher:
Oxford University Press
DOI:10.1093/acprof:oso/9780198516002.003.0003

Dislocations are the most effective carriers of plasticity in crystalline solids. Under normal circumstances, they are readily generated by purely topological convolution processes as in Frank-Read sources or by double cross slip of screw dislocations, which can in turn produce new Frank-Read sources readily, all at relatively low levels of stress. In BCC metals and strongly directionally bonded solids, the glide of dislocations in their slip planes are resisted by a substantial lattice resistance at low temperatures giving these materials a high intrinsic plastic resistance to begin with. In comparison, in pure close packed FCC and HCP metals the lattice resistance in the best slip systems is normally very small, making it necessary to introduce other extrinsic mechanisms to raise the plastic resistance. This is most effectively accomplished by alloying with a second constituent, which either in the form of a solid solution or as precipitate particles in the host metal can very effectively elevate the resistance to dislocation motion. This chapter starts with a discussion of why a dislocation mechanics view is essential for properly understanding the remarkable effectiveness of strengthening by small volume fractions of second constituents either in solution or in the from of nano-meter sized precipitates, which is both qualitatively and quantitatively missed by a heterogeneous continuum plasticity approach. Following this comparison, the major strengthening mechanisms that will be developed in greater detail in Chapters 4-8 are listed briefly.

Keywords:   dislocation mechanics, continuum plasticity, continuum composite theory, Frank-Read sources, double cross slip, BCC metals, FCC metals, HCP metals

Oxford Scholarship Online requires a subscription or purchase to access the full text of books within the service. Public users can however freely search the site and view the abstracts and keywords for each book and chapter.

Please, subscribe or login to access full text content.